BioUniversal KFG+

BioUniversal KFG+ is a reduced-gold universal alloy for the economical production of restorations using the milling and double crown techniques. This alloy is suitable for veneering with low-fusing special ceramics and laboratory composites.

Indications*

Telescope crowns, conus crowns
Bridges
Wide-span bridges
Cast posts / cores, bars, attachments
Implant-supported superstructures
Partial dentures

Technical Data

Composition (%):	Au 37.7 \| Pd 15.9 \| Ag 32.6 \| In 12.2 \| Pt <1.0, Ir <1.0, Rh <1.0, Sn <1.0, Li <1.0, Fe <1.0, Nb <1.0
ISO	22674:2016
ADA Class	Noble
Type / Color	4 / Yellow
Density (g/cm³)	12.2
Melting Range (Solidus/Liquidus):	920 - 995 °C
Elastic Modulus (GPa):	95
	As Cast Porcelain Fired Hardened
Vickers Hardness:	230 200 225
Tensile Strength (MPa):	600 560 610
0.2% Proof Stress (MPa):	470 430 495
Elongation (%):	5 5 3

Advantages

Economical use due to low density
Cu-free
Excellent milling characteristics, especially for the double crown technique
Compatible with low-fusing special ceramics and laboratory composites (e.g. SR Nexco)
Certified biocompatibility

Processing Data

Investment Material:	Phosphate-bonded / Gypsum-bonded
Preheating / Burn- out Temperature:	625 - 710 °C
Crucible	Ceramic crucible
Casting Temperature:	1060 - 1120 °C
Oxidation °C/min/Vacuum:	700 / 1 / Yes
CTE:	(25 – 500 °C): 17.0 x 10^-6 /K
Recommended Lab Composite:	SR Nexco
Laser Welding Wire:	Laser C&B Yellow

*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES