Euro 33 Implant

Euro 33 Implant is a high strength ceramic alloy. This high strength together with high heat resistance allow accurately fitting casting objects to be produced, especially for implant-supported superstructures.

Indications*

Crowns
Telescope crowns, conus crowns
Bridges
Wide-span bridges
Cast posts / cores, bars, attachments
Implant-supported superstructures
Partial dentures

Technical Data

Composition (%):	Pd 43.9 \| Au 28.0 \| Ag 19.5 \| Sn 4.8 \| In 3.5 \| Ru <1.0
ISO	22674:2016
Type / Color	4 / White
Density (g/cm³)	12.3
Melting Range (Solidus/Liquidus):	1220 - 1290 °C
Elastic Modulus (GPa):	113
	Porcelain Fired Hardened
Vickers Hardness:	230 260
Tensile Strength (MPa):	720 760
0.2% Proof Stress (MPa):	470 500
Elongation (%):	18 17

Advantages

High mechanical strength
Excellent processing and polishing properties
Economical due to low density
High heat resistance
Compatible with conventional metal-ceramics (e.g. IPS Style)

Processing Data

Investment Material:	Phosphate-bonded
Preheating / Burn- out Temperature:	900 °C
Crucible	Ceramic crucible
Casting Temperature:	1430 °C
Oxidation °C/min/Vacuum:	950/5/Yes
CTE:	(25 – 500 °C): 14.3 x 10^-6 /K
Recommended Metal Ceramic:	IPS Style, IPS InLine
Laser Welding Wire:	Porta P6

*See TYPE CLASSIFICATION DUE TO PHYSICAL PROPERTIES